Material Characterization of Self Assembled Copper-Silicide Nanostructures on Si(001), (110), and (111)

Download (4.66 MB)
thesis
posted on 2014-10-28, 00:00 authored by Poh Keong Ng
Metal-silicide is a compound formed between metal and silicon (Si), which have a wide variety of properties, e.g. metallic in TiSi2, thermoelectric in ReSi1.75, photonic in Mg2Si, semiconducting in Ca3Si4, and superconductivity in LaSi2. A lot of these properties can be enhanced when fabricated at the nanoscale regime. While there is a lot of research focused on metal silicide nanostructures, copper-silicide (Cu-Si) nanostructures are seldom studied. Only recently, Cu-Si nanostructures were discovered to have optical properties in the mid Infra-Red range and act as catalysts in the CVD growth of Si nanowires. Most of these studies were conducted on free standing Cu-Si nanowires, whereas studies on planar or horizontal Cu-Si nanostructures are rare. Therefore, the focus of this thesis is to characterize the basic properties of planar Cu-Si nanostructures that were fabricated on Si(001), Si(110), and Si(111). In this thesis, material composition was characterized with X-ray energy dispersive spectroscopy (XEDS) whereas the crystallography was characterized with electron diffraction pattern in transmission electron microscopy. The thesis work also extends to in situ electrical resistivity and failure current density measurements of Cu-Si nanowires. Finally, size effects of sub 100 nm Cu-Si nanostructures on electronic properties were studied with a scanning tunneling microscope (STM).

History

Advisor

Lilley, Carmen

Department

Electrical and Computer Engineering

Degree Grantor

University of Illinois at Chicago

Degree Level

  • Doctoral

Committee Member

Dutta, Mitra Stroscio, Michael Bode, Matthias Guisinger, Nathan

Submitted date

2014-08

Language

  • en

Issue date

2014-10-28

Usage metrics

    Categories

    No categories selected

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC